A weakly alkaline process for high speed for selective plating in continuous lines producing a semi-bright to bright appearance.
Excellent bonding and solderability are seen together with low porosity and freedom from cracking.
A brilliant, high gloss process designed for decorative and technical applications e.g. spectacle frames and jewellery. Crack free deposits of up to 3 µm are produced and it is suitable for both rack and barrel application.
Palladium 459 is a weakly alkaline electrolyte for the deposition of light, bright coatings up to a thickness of 0.5 µm.
This process is ideal for use as a palladium strike bath.
PALLUNA ACF-100 is ammonia and chloride free and produces coatings of 80:20 palladium nickel for reel to reel applications.
The deposit exhibits low internal stress and good corrosion resistance.
PALLUNA ACF-200 is ammonia and chloride free and produces coatings of 80:20 palladium nickel for PCB applications.
The coating has excellent wear resistance and is ductile.
PLATUNA N1 produces white and ultra bright platinum coatings up to 1µm thick.
The process is easy to operate and can be used in rack or barrel applications.